Why Is Titanium Alloy A Difficult Material To Process?
Source: | Author:pmo7b64f4 | Publish time: 1090 days ago | 612 Views | Share:

Why do we think titanium alloy is a difficult material to process? Because of the lack of a deep understanding of its processing mechanism and phenomena.
1. Physical phenomena of titanium processing
The cutting force of titanium alloy processing is only slightly higher than that of the same hardness, but the physical phenomenon of processing titanium alloy is much more complicated than that of processing steel, which makes the processing of titanium alloy face great difficulties.

Most titanium alloys have very low thermal conductivity, only 1/7 of steel and 1/16 of aluminum. Therefore, the heat generated during the cutting of the titanium alloy is not quickly transferred to the workpiece or carried away by the chips, but accumulates in the cutting area, and the temperature generated can be as high as 1 000 ° C or more, causing the cutting edge of the tool to rapidly wear, crack and The formation of built-up edges, the rapid emergence of worn edges, and the production of more heat in the cutting area, further shortening the life of the tool.

The high temperatures generated during the cutting process also destroy the surface integrity of the titanium alloy parts, resulting in a decrease in the geometric accuracy of the parts and a work hardening phenomenon that severely reduces the fatigue strength.
The elasticity of titanium alloys may be beneficial to the performance of the part, but the elastic deformation of the workpiece during the cutting process is an important cause of vibration. The cutting pressure causes the "elastic" workpiece to leave the tool and bounce, so that the friction between the tool and the workpiece is greater than the cutting action. The friction process also generates heat, which increases the problem of poor thermal conductivity of the titanium alloy.
This problem is exacerbated when machining thin-walled or toroidally deformable parts, and it is not an easy task to machine titanium alloy thin-walled parts to the desired dimensional accuracy. Because the local deformation of the thin wall has exceeded the elastic range and plastically deformed as the workpiece material is pushed away by the cutter, the material strength and hardness of the cutting point are significantly increased. At this time, the machining becomes too high according to the previously determined cutting speed, which further causes the tool to wear sharply.
"Hot" is the "culprit" of difficult machining of titanium alloy!

2. Process for processing titanium alloy
Based on the understanding of the processing mechanism of titanium alloys and the previous experience, the main processes for processing titanium alloys are as follows

(1) Blades with positive-angle geometry to reduce cutting forces, cutting heat and deformation of the workpiece.

(2) Maintain a constant feed to avoid hardening of the workpiece. The tool should always be in the feed state during the cutting process. The radial feed amount a e should be 30% of the radius during milling.

(3) High-pressure and high-flow cutting fluid is used to ensure the thermal stability of the process and prevent the surface of the workpiece from being denatured and the tool from being damaged due to excessive temperature.

(4) Keep the blade edge sharp, the blunt tool is the cause of heat build-up and wear, which can easily lead to tool failure.

(5) As far as possible in the softest state of titanium alloy, since the material becomes harder to process after hardening, the heat treatment increases the strength of the material and increases the wear of the blade.

(6) Use a large tool nose radius or chamfer to cut in as much as possible into the cutting. This can reduce the cutting force and heat at every point and prevent local damage. When milling titanium alloy, the cutting speed of each cutting parameter has the greatest influence on the tool life vc, and the radial cutting amount (milling depth) ae is second.

3. Solve the problem of titanium machining from the blade

The blade groove wear that occurs during the processing of titanium alloys is the local wear of the back and front in the direction of the cutting depth, which is often caused by the hardened layer left by the previous processing. The chemical reaction and diffusion of the tool and the workpiece material at a processing temperature exceeding 800 ° C is also one of the causes of groove wear. Because during the processing, the titanium molecules of the workpiece gather in the front area of the blade, and "weld" to the blade at high pressure and high temperature to form a built-up edge. When the built-up edge is peeled off from the blade, the cemented carbide coating of the blade is carried away, so titanium alloy processing requires special blade materials and geometries.

4. Tool structure suitable for titanium machining

The focus of titanium machining is heat, and a large amount of high-pressure cutting fluid must be sprayed onto the cutting edge in time to remove heat quickly. There is a unique structure on the market for milling cutters specifically for titanium machining.

10000拍拍18勿入免费看,国产美女精品自在线拍免费,XX00欧美极品少妇,偷拍小说区图片区视频区 <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <蜘蛛词>| <文本链> <文本链> <文本链> <文本链> <文本链> <文本链>